LDPE, HDPE, PP, Teflon Resistance

LDPE & HDPE resistance listed by chemical

1.4-dioxane LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days.  Acetaldehyde LDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
LDPE at 50°C: immediate damage may occur. Acetic Acid 5 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Acetic Acid, glacial 50% LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50 °C: immediate damage may occur. Acetone LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use. Allyl Alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Aluminum salts LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Amino acids LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Ammonia LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Ammonium carbonate saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Ammonium phosphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Ammonium sulphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Amyl chloride HDPE at 20°C: shows some effect after 7 days.
HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur.
Not recommended for continuous use. Aniline LDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.  Benzene LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use. Benzyl alcohol LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.  Boric acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Bromine LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.  Butyric acid LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.  Calcium chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Calcium hydroxide saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Carbon tetrachloride HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C & HDPE at 50°C: show some effect after 7 days.
LDPE at 50°C: not recommended. Chlorine 10% in water LDPE / HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 50°C: shows damage and is not recommended. Chlorobenzene Immediate damage may occur.
Not recommended for continuous use. Chloroform LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: immediate damage may occur.
Not recommended for continuous use. Chromic acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Chromic acid 50% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Citric acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Cresol HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use. Cyclohexane LDPE / HDPE at 50°C: immediate damage may occur.
LDPE / HDPE at 20°C: show some effect after 7 days. Diethyl ketone LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use. Dimethylsulfoxide LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Ethanol 95% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Ethyl acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Ethyl benzene HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use. Ethylene glycol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Ethylene oxide HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days.  Ferric chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Fluoride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Fluorine HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: shows some effect after 7 days.
Not recommended at 50°C. Formaldehyde 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Formaldehyde 40% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Glycerol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hexane HDPE at 20°C: shows little or no damage after 30 days continuous use.
HDPE at 50 °C: shows some effect after 7 days.
LDPE not recommended at any temperature. Hydrochloric acid 20% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hydrochloric acid 35% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hydrochloric acid 5% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hydrocyanic acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hydrofluoric acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hydrofluoric acid 4% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hydrofluoric acid 48% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hydrogen peroxide 3% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Hydrogen peroxide 30% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Isobutyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Isopropyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Kerosene LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE not recommended at 50°C, as immediate damage may occur. Lactic Acid 10 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Lactic Acid 90 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Lead acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Methanol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Methyl ethyl ketone Immediate damage may occur.
Not recommended for continuous use. Methyl propyl ketone HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use. Methylene chloride HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use. Mineral oil LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: may show immediate damage and is not recommended. n-amyl acetate LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days or constant exposure. n-butyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Nitric acid 50 % LDPE at 20°C: shows little or damage after 30 days.
HDPE at 20°C & LDPE at 50°C: show effect after 7 days.
HDPE at 50°C: shows immediate damage and is not recommended. Nitric acid 70 % LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended. n-octane LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Oleic acid HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C-50°C: shows immediate damage and is not recommended. Oxalic acid LDPE at 20°C: shows some effect after 7 days.
HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days.  Ozone LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended. Perchloric acid LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended. Perchloric ethylene LDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended. Phenol LDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended. Phosphoric acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Phosphoric acid 85% LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows immediate damage and is not recommended. Phosphorous trichloride LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days.  Potassium carbonate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Potassium hydroxide 5 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Potassium hydroxide concentrated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Potassium permanganate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Propylene glycol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Pyridine Immediate damage may occur.
Not recommended for continuous use. Salicylic acid, saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Silver acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Silver nitrate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sodium carbonate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sodium chloride, saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sodium dichromate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sodium hydroxide 1% LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C-50°C: shows some effect after 7 days.  Sodium hydroxide 50% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sodium hypochlorite 15% HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C: is suitable but at 50°C: shows some effect after 7 days.  Sodium nitrate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sodium sulphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sucrose LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sulfuric acid 20% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sulfuric acid 6% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sulfuric acid 60% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Sulfuric acid 98% LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C: shows effect after 7 days.
Not recommended for use at 50°C. Tannic acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Tetrahydrofuran LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended. Toluene LDPE at 20°C: show some effect after 7 day of constant exposure.
HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage.
Not recommended. Trichloracetic acid LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended. Trichlorethane Immediate damage may occur.
Not recommended for continuous use. Turpentine oil LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended. Urea LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.  Xylene HDPE at 20°C: shows some effect after 7 day of constant exposure.
LDPE at 20-50°C and HDPE at 50°C: show immediate damage.
Not recommended. Zinc chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.