As previously stated, the friction material is the most important brake pad layer, as it constitutes, together with the disc, the friction pair, and its composition determines the coefficient of friction and durability of the pad [ 28 ]. By taking advantage of the gap in the available materials this review will continue to describe the materials most commonly used in the manufacture of brake pads, and their role and impact on the tribological properties of the final product.
NFJ supply professional and honest service.
There are also manuscripts by researchers who decided to comprehensively review friction materials and their components. Naresh Kumar and Suman [ 21 ] described the research results of various conventional brake pad components in a very broad way. However, there is no information on non-standard materials, e.g. by-products from food production processes. Yang et al. thoroughly described modern nano friction materials in their review [ 22 ]. However, conventional materials were omitted, which still constitute the vast majority of the brake pad composition. Kato in his manuscript described typical wear behaviors of representative materials of coatings, composites, metallic alloys and ceramics in relation to their friction behaviors [ 23 ]. Unfortunately, other material properties have not been described. Chan and Stachowiak [ 24 ] made a very good review. They took into account the division of friction materials and described their properties. Unfortunately the article was published quite a long time ago, so it does not include new solutions. The same is the case with other works that require updating [ 25 , 26 , 27 ].
The literature analysis allowed to notice that there is a lot of publications devoted to the review of materials for the friction materials production. However, many researchers focus on a narrow range of speciality. Bevilacqua et al. for example focus on catalytic oxidation of carbon &#; carbon composites used in aircraft brakes [ 14 ]. Awasthi and Wood [ 15 ] dealt with a similar subject, but much earlier. These articles describes the advantages of these materials and assessed their applicability. Shojaei et al. in turn considered rubber-based composite friction materials. Their main application is for railroad brakes. The influence of rubber-based additives on the thermal conductivity of the final product was also analysed [ 16 ]. Fiber reinforced polymers for applications in modern vehicles was the subject of a review by Bijwe [ 17 ]. This work presents new achievements in the reinforcement of friction materials with non-asbestos fibers. In India, the focus was on aluminum-alumina arrangement of composite materials dedicated for the automotive industry [ 18 ]. This group of materials was developed to replace the harmful asbestos. Kryachek was also involved in the review of composite materials [ 19 , 20 ]. In his works detail properties, research methods and results, as well as new methods of obtaining were discussed.
Matters are different for brake pads. Their structure is far more complicated. Brake pads have specific layers ( Figure 2 ), the most important of which is the friction layer &#; layer that we brake during the normal operation of the brake pad [ 11 ]. It is usually 6 to 9 mmthick. Its composition differs significantly and is adjusted to specific purposes. Beneath the friction material is the so-called underlayer. It is 1-4mm thick and acts as an adhesive holding the friction material. The underlayer is placed on a thin (usually under 1 mm) layer of a base coat which improves its grip to the &#;spin&#; of the brake pad, the back plate. The base coat also ensures a certain level of thermal isolation. This is to prevent excess heat from reaching the braking fluid. The back plate provides the necessary stiffness of the brake pad, and allows it to move along the guide of the calliper thanks to profiled edges [ 12 ]. Some manufacturers place special anti-noise shims in order to reduce the amount of unfavorable noise during braking [ 13 ].
Most vehicles manufactured today use disc brakes ( Figure 1 ). The main element of this type of design is the disc, spinning alongside the road wheel, and the brake pad, connected with the hub via a calliper [ 4 ]. As the pad is pressed against the disc, friction occurs which transforms kinetic energy into heat. The energy, in the form of heat, is then released into the atmosphere [ 5 , 6 ]. This is a necessity, as excess heat may damage the suspension elements, which are made from plastics, or even tires [ 7 ].
The significance of the braking system in any vehicles is enormous. Its main function is reducing the speed of the moving vehicle or stopping it completely. The braking system must therefore be reliable, and the efficiency of brakes must remain constant throughout their lifespan and in changing atmospheric conditions [ 1 , 2 ]. The wellbeing and life of the vehicle&#;s passengers rests upon it, but also of other, accidental participants of road and pedestrian traffic [ 3 ].
carbon-carbon &#; structure of the pad is similar to that of ceramic pads, yet its properties are more desirable, namely: high coefficient of friction, resistance to increased temperatures and wear, small weight; this type of brake pad works best in elevated temperatures, that is why it is often used in sport cars; manufacturing costs, compared to conventional brake pads, are very high;
non-asbestos organic or ceramic &#; the main component in this case is an organic material usually reinforced with aramid, glass or ceramic fiber; this design ensures high durability, resistance to high temperature, low wear rate, light weight and quiet operation; however, due to the complexity of the production process, this type of solutions may be very expensive, and because of high hardness, the material may be brittle;
Abrasives are used for modifying (increasing or decreasing) the coefficient of friction. Additives such as steel, cast iron, flame resistant oxides and silicates or quartz, due to their hardness, are used for increasing the coefficient of friction between the brake pad and disc, and therefore increasing the operating life of the pad. Additionally, the effect is reinforced by the adhesion with the disc material, especially in terms of metals. The substances also create contact zones, which are the main friction areas in the pair of elements [ 41 , 42 ]. Unfortunately, due to friction in the contact areas, excessive temperatures are generated. This may lead to destruction of the pad&#;s structure and lead to separation of its components. That is why lubricants are used, which usually improve the thermal conductivity of the pad. Lubricants improve the removal of energy from the contact area and prevent the friction elements from overheating [ 43 , 44 , 45 ]. The most common lubricants are metallic sulphates (such as copper or tin) and graphite. Their lubricity depends on the content in the pad (approximately 10% of volume yields the best results) and the size of lubricant particles [ 46 ].
Fillers are used to filling up the empty spaces between the other components of the brake pad. They can make up for up to 10% of the brake pad volume, which is why using the right substance is so important. Most common fillers include vermiculite, perlite, mica, barium sulphate, and calcium carbonate, due to the substances&#; resistance to high temperature, lack of reaction with other components of brake pads, and low price [ 40 ]. Further on in the work, less common fillers are also analyzed.
The reinforcement is a fibrous material (one or more) which improves the binder&#;s mechanical properties (increasing its strength). Different types of reinforcement materials have a significant impact on the durability and resistance of the brake pad, therefore, the selection cannot be random. In the past, asbestos was an excellent reinforcement fibre. However, due to its harmful properties [ 37 ], it was necessary to find a replacement (which today is no problem at all, since there is a whole range of materials which can be used successfully to this end [ 38 , 39 ]).
The binder is the flue that hold all the components of the pad. This substance must be characterised by high and stable coefficient of friction, resistance to high and rapidly changing temperatures, and low mass (the binder usually makes up approximately 20% of the pad volume) [ 36 ]. Also, the material must not react with any other component of the pad, as this might lead to changes in overall material characteristic or cause delamination of the composite and greatly limit the efficiency of the braking system. The binder is usually made from epoxy or silicone resin [ 24 ].
Brake pads manufacturers utilise approximately different materials [ 29 ] which have different effects of the final product. An average brake pad consists of from 10 to 20 different substances [ 30 ]. Selecting the right composition for the brake pad and predicting its impact on the final products is a difficult task. It requires tremendous amounts of research and abundant experience [ 31 ]. The decision must also take into account the intended use of the brake pad, and their operating conditions. The final properties of the brake pad are also shaped by production technology, which is usually the best kept trade secret of every manufacturer. Effective production technology may improve the tribological properties of the brake pad by 100% [ 32 , 33 ].
As a binding material, resins are often used as binders. They must be added in precisely determined amounts, as only then will they properly serve their desired function [50]. Too little resin reduces the durability of the pad, too much resin may reduce the coefficient of friction in high temperatures and significantly increase hardness [51, 52]. Resin is one of the most important components used in the manufacture of brake pads, as it binds all of the other components of the pad, allowing them to effectively cooperate. However, when excessive heat is generated during braking, the quality of the material of the brake pad may deteriorate. This is related with degradation of resin resulting in the substance losing its binding properties [53]. That is why the thermal stability of a brake pad, its capacity for maintaining mechanical properties and capacity for binding components in unfavorable conditions of braking may largely depend on the resin [54]. In order to improve the original mechanical and thermal properties of resins, numerous attempts at modifying its composition are made [55, 56].
Phenol resins are the most often filler produced almost exclusively for the purpose of friction materials. They have hardly any other uses. The weight fraction of phenol resin in a brake pad ranges from 5 to 35% of volume. The amount of content affects the coefficient of friction value and the ware rate inversely. The COF value change is only a few percent heaving about 10% drop in the wt. pad resin content [57]. Its common use in the automotive industry stems from the resins favourable properties, such as high mechanical resistance and low price [58]. What is also important, this type of resin has a low thermal expansion. Compared to other resins, it is also more resistant to solvents, acids, and water, and generates less smoke during combustion. The temperature of the initial degradation, which is very important because of correlation with the phenomenon of the brake pad fading, decreases from 354&#;C of the pure resin to 303&#;C of the cured friction material [59]. Unfortunately, the material is brittle. Susceptibility to cracking may be reduced by adding oil or silicone gum. This produces silicone resin. However, in the process other mechanical properties suffer [29]. Phenol resin is not the best material for high temperature friction. During sudden braking, the temperature of the pad may easily reach 700&#;C, greatly exceeding the degradation temperature of phenol resin [60, 61].
Figure 4
Figure 5
COPNA resin demonstrates slightly improved thermal resistance. Although its disintegration temperature is similar (400-500&#;C), significantly less gas is released in the process. This reduces the risk of brake fading. Also, as the particle is similar to graphite, the two materials bind together excellently. This improves the pad&#;s friction resistance [62, 63].
Cyanate ester resins are made from cyanide monomers. These resins are chemically neutral and demonstrate a tendency to damper vibration. However, its most important property is resistance to high temperatures. Research has shown that enriching it with ZrB2 in the amount of about 5% improves thermal stability and ensures optimal tribological properties related to the COF and wear rate [64]. Experiments were also carried out with admixture of graphite and MoS 2. That way scientists obtained an improvement in mechanical properties and a decrease in the wear rate [65]. The high cost (resulting from a complicated and often multi-day production process [66]), on the other hand, is one of its main drawbacks. That is why it is rarely used in friction materials. Cyanate ester resins find more applications in electronics [67, 68].
Epoxy resins are very commonly used in the industry. Their low resistance to heat (degradation starts at approximately 260&#;C) make them unfit for friction materials [69]. The results of some researchers show that even at a temperature of 100&#;C, aweight loss of about 7% can be noted [70]. This mass loss can be associated with the formation of volatiles during firing. Continued heating above 400&#;C led to the formation andoxidation of carbon. However, interesting results are obtained when epoxy and phenol resins are combined. The material is far more resistant to high temperatures, and has better mechanical properties than the two resins [69].
Figure 6
Figure 7
Figure 8
Figure 9
Thermoplastic polyamide resin is a product obtained from fluoresin and calcium carbonate. It is resistant to wear and high temperatures. Also, the production process is inexpensive and easy. However, the resin is a good thermal isolator (approximately three times better than phenol resin). That is why its usefulness in the manufacture of brake pads is very small [69].
Metal matrix composites are increasingly found in the latest solutions of the automotive industry. These matrices are used not only in braking systems, but also in clutches [71], intake systems [72], engine blocks [73], or fuel system elements, mainly classic injectors using piezoelectric stacks [74, 75], as well as alternative fuels injectors [76]. These composites are also used as a partial or complete replacement for conventional materials in the production of monoqocue type frames [77]. In brake systems, metal matrix composites are usually used for the production of brake drums and discs, both in cars [78, 79, 80] and in other types of vehicles, such as motorcycles [81]. In the friction linings of brake pads, mostly aluminum-based materials reinforced with, for example, silicon carbides, are used [82]. Their excellent properties such as: low density, good mechanical strength, resistance to high temperatures and good thermal conductivity [83, 84, 85] are features that are desirable in brake pads. Unfortunately, materials of this type also have their drawbacks. Issues with uniformity of distribution of SiC particulates, residual porosity, formation of undesirable phases such as aluminum carbide, and high temperatures incurred during braking effectively limit their common use in brake systems [85]. The last feature is related to the high coefficient of friction when cooperating with other materials, and overheating may lead to material degradation [86]. Very important issue is related with MMC production techniques: liquid-metal-mixing processes (incorporation of reinforcement particles or short fibers into a molten or semi-solid aluminum matrix through a stirring process), liquid-metal-infiltration processes (molten aluminum or its alloy is moved into a preform of the reinforcement, either as a packed bed or a rigid, free-standing structure) and solid-state processes (e.g. powder metallurgy) [87]. These are methods that require far more sophisticated equipment and deeper knowledge than those used in the production of resin-based friction materials.
Figure 10
Aramid is a material made from rigid molecular chains oriented along fibre axes. This structure makes it possible to utilise the covalent bonds along the polymer, producing a high Young modulus and durability higher than steel wire of the same weight [88, 89, 90]. It is sold under many trade names, the most popular of which is Kevlar. Aramid fibres are an excellent alternative to asbestos. That is why they are used as reinforcement in brake pads [91]. The material performs well in high temperatures, which has a positive effect on the stability of the coefficient of friction [92]. Unfortunately, the use of aramid reduces the coefficient of friction even by half. On the other hand, the wear rate is improved by up to ten times [93, 94]. Importantly, changing the percentage of aramid content does not cause a linear change in the properties of the final material. Research has shown that an aramid fiber content of 6% of total volume is the optimal solution. The value of coefficient of friction doesn&#;t change much with temperature rising. Its value is approximately 0.41 [95, 96]. The use of Kevlar mixed with glass or steel fibres is an interesting solution. This produces a hybrid material which is cheaper than pure aramid and provides favourable properties confirmed in numerous studies [97, 98, 99].
Glass has been used in the industry for a long time. With the ban on asbestos, the automotive industry started researching the use of glass (in the form of glass fibres) as a suitable substitute [100, 101]. The results obtained by some researchers indicated that the material has positive mechanical properties (especially hardness and abrasion resistance) [51, 102]. The highest values of COF (0.41-0.44) were obtained for samples with 5-10 wt% of glass fibers content. The samples also consisted of: silicon carbide, coconut fibre, graphite, alumina oxide, zirconia oxide and resin [103]. On the other hand, it was also observed that, depending on the operating temperature, the pad materials with glass fibre content have varied capacity for creating film on the brake disc. This results from the destruction of the binder and &#;pulling out&#; of fibres, which then deposit on the friction pair [104, 105]. This may lead to increased degradation of the pad, undesired vibration and noise, especially in high (10% volume) glass fibre content. Researchers believe this is also caused by the brittleness of glass. These negative features were partially reduced by the use of shorter fibres [100, 106, 107]. Aranganathan et al. discovered that the size of the glass fibers used to produce the friction material is also important. Milled glass fibers exhibited a higher coefficient of friction, high wear rate, and larger oscillation amplitudes during stick &#; slip experiments, which was attributed to the higher static friction due to the smooth surface. The friction materials with milled glass fibers, therefore, can have a higher propensity for friction-induced vibration during brake applications [108]. It is also worth noting that glass has a high melting temperature (over &#;C) and is a good thermal insulator [109]. While the former property is beneficial in brake pads as it stabilizes the coefficient of friction, the latter one is rather avoided.
Figure 11
Figure 12
Cocoa beans are chiefly used in the food industry. The outer shell of the bean (Cocoa Bean Shells &#; CBS) is a food processing waste material, a by-product. Because it is a low density fibrous material, it was attempted to use it as a substitute for asbestos. Non-toxicity of the material is one of its greatest advantages [110, 111]. In many countries (such as Nigeria) it is very cheap and easily available, and using it in the automotive industry solves the problem of utilization [112]. Olabisi et al. studied the density, water and oil absorption, abrasion resistance, coefficient of friction, thermal conductivity, hardness, as well as compression and tensile strength of three groups of pads, in which the CBS content was 21, 26, and 31% volume. The results were compared with the average values obtained in testing conventional brake pads. The researchers observed that CBS fibre content increases the pad&#;s capacity for water and oil absorption. All of the studied material also showed lower density in comparison to conventional brake pads, which had a positive effect on the weight of the final product. It was also shown that the pads have lower coefficient of friction and abrasive wear rate. This increased the durability of the brake pad. However, cocoa bean shell fibres do demonstrate decent thermal conductivity, compared to pads based on other components. Despite low hardness, brake pads containing CBS (especially higher contents) showed improved resistance properties, compared to conventional pads [112].
Palm Kernel Shell is a waste material obtained, for example, in the production of palm oil used in margarine. Palms are mainly grown in plantations in West Africa. 15-18 ton yield per hectare make PKS (Palm Kernel Shells) an abundant and cheap material. Its low density (compared to other organic waste) makes it easy and inexpensive to transport [113]. PKS, due to its fibrous structure, is used as an asbestos substitute in brake pads. Their content can reach even 40% of the friction layer volume [114]. Pulverized particles demonstrate low hygroscopic properties and high stiffness and hardness, which are favourable properties in brake pads [115]. They are also characterised by high coefficient of friction (approximately 0.41) with a cast iron brake disc. However, due to its low resistance to high temperatures, it was shown that during braking from high speeds the coefficient of friction significantly decreased. Oxidation also increased the wear of the pad, which was significantly quicker in comparison to commercial brake pads [116, 117]. Conducted by Mgbemena et al. research showed the following onset temperatures for the three phases: 54.28&#;C, 237.14&#;C and 538.57&#;C respectively and considerable weight loses of 6%, 27% and 42.37% [118]. Test of brake pads intended for &#;cold&#; braking, which does not produce temperatures in the hundreds of degrees C, yielded far more success. The size of the PKS particle used in the production of the pad is also important. Brake pads containing larger particles showed improved hygroscopic absorption and better wear resistance in tests. The best mechanical properties (i.e., high hardness and resistance and low porosity) was obtained when using finely pulverized PKS [119].
Figure 13
Figure 14
Banana peels constitute up to 40% of the total weight of a fresh banana [120]. Currently the peels are used as fertilizer or discarded as waste [121]. According to the criteria established by the National Cancer Standard Institute [122], banana peels are classified as non-toxic for human tissues, and therefore can be safely used in various industries. Physical and chemical tests on banana peels showed that they are mainly made of antioxidants and pectin [123]. Pectin substances are complex polysaccha ride mixtures containing galacturonic acid units as the main chain acting as the gel forming agent. The harness of the substance is further increased by adding banana peel powder. It was observed that as temperature increases, the powder initially becomes more gelatinous, and then hardens [124, 125]. Because of these properties, banana peels can be used for forming novel brake linings, increasing the capacity of binding resin in high temperatures. Experimental tests confirm these claims. Sufficiently strong bonds between powdered banana peels resulting in an increased coefficient of friction [126]. Additionally, the material showed low water and oil absorption. However, brake pads containing banana peels wear more quickly [125].
Figure 15
Periwinkle shell is the most unusual material used in the production of brake pads presented in this paper. The shells of these tiny animals are a waste by-product of food processing. Due to the huge amount of waste produced in the process, it is believed to be a threat to the environment and human health. The use of fragmented shells (as an alternative to asbestos) in the production of brake pads may partially reduce the issue of utilization. Scientists in Nigeria studied the mechanical properties of the shells using pulverized material with particle size under 255 μm. Their research showed that the material has lower density than asbestos and is quite resistant to high temperatures. First signs of thermal degradation were observed at temperatures exceeding &#;C. It was also shown that the studied material is harder (approx. 75 HRC) than asbestos [127, 128]. Other researchers, also based in Nigeria, went further and produced a range of brake pad prototypes using various sizes of periwinkle shell particles (ranging from 100 to 350 μm). The studies showed that 100 μm particles offer the best properties. They presented the best compression resistance and hardness, and lowest water and oil absorption. According to the authors, the parameters are better than those of commercial brake pads [129]. The results were confirmed by Amaren et al. In their research, the smallest fractions (125 μm) gave the best abrasive wear resistance results [130].
Ceramic composites are materials made in at least two phases: the binder and the reinforcement (component) embedded in the binder. One of the most common combinations used in the automotive industry is silicon carbide (the binder) and carbon fibre (the reinforcement supporting the structure). Thanks to their structure, ceramic composites are characterised by favourable mechanical properties, such as high durability and resistance to wear (the operating life of braking systems utilising C/SiC may be five times longer compared to conventional solutions), resistance to high and rapidly changing temperatures, low thermal expansion, and light weight [131]. The main disadvantage of this type of material is the instability of the COF. Research has shown that depending on the friction conditions, the COF value can vary from about 0.2 to even 0.8 [132]. Moreover, production process requires specialised equipment and is time consuming, resulting in a costly final product [133, 134, 135]. Another group of materials combine aluminium alloys and silicon carbide (Al/SiC). This type of composite is supposed to reduce inertia (which is particularly important for brake discs) and noise, and to increase wear resistance, as well as harmonise the friction mechanism. Additionally, the use of Al/SiC composites makes it possible to control heat conductivity by selecting the content and distribution of the reinforcing material [136, 137]. Unfortunately, few brake pad manufacturers have yet introduced this type of product.
Figure 16
Contact us to discuss your requirements of Inorganic high-temp brake lining powder. Our experienced sales team can help you identify the options that best suit your needs.
Figure 17
Barite is a mineral mined in several locations around the globe. It shows high density and tribological properties which change only slightly with rising temperatures. The availability of the mineral makes significantly reduces its cost. Barite is used as a brake pad filler [51]. Sugözü and Dağhan showed that as the barite ratio in a brake pad increases, the wear rate reduces, despite the mineral&#;s resistance to abrasion. It also reduces the coefficient of friction [138]. El Soeudy et al. add information, that barium sulfate has a little effect on the negative gradient of the coefficient of friction (its value is from 0.3 to 0.7 depending on composition of the sample) with sliding velocity and rubbing pressure changes. They also discovered that increase of BaSO4 content in friction material causes high stability of the coefficient of friction (high fade resistance) and leads to better wear rate (low wear resistance) [139]. Moreover, barite is resistant to high temperatures. Laboratory tests have shown that it does not significantly change its properties at temperatures above 300&#;C [140].
Fly ash is a by-product of coal combustion in industrial factories and heat and electricity plants. It has the form of fine mineral dust, light to dark grey or light brown colour, and is mainly composed of silicon, aluminium, and iron. Also, fly ash contains various trace elements, similarly to natural rock, and has small content of unburned carbon [141]. Coal combustion has a negative impact on the environment, which is why waste product management, especially in terms of industrial waste, is an environmental policy priority in many states. Different types of coal and varieties of power boilers result in fly ash with changing properties, which impacts the waste management process [142, 143]. As the material is cheap, it was attempted to use it as a filler in brake pads. The mass content ranges from several percent to 55-60% of total weight [144, 145]. Research showed that brake pads with high ash content have stable coefficients of frictions, but only for low initial speeds of the vehicle. Some researchers observed that after reaching a limit value (the tests were based on braking from an initial speed of approx. 100 km/ h), the coefficient of friction significantly decreased [146]. This could be the result of using other materials, which are not as resistant to high temperatures. Different results were obtained by Sugözü. In his research, the value of the coefficient of friction in cooperation with cast iron is constant, or even rising with the temperature. It reaches little more than 0.3 at operating temperatures of 200&#;C. The sample used in the study contained 46% of ash [147]. Choosri et al. in turn had the best results for samples containing only 4 wt% of considered material [148]. The results are not unequivocal, therefore it can be assumed that the selection of the other components of the abrasive material has a decisive influence. Fly ash itself does not change its properties with rising temperatures [143]. Ash has a positive effect on thermal energy management. Brake pads with a 55% volume ash content were less susceptible to heat than commercial pads. This results from high heat capacity of fly ash (up to 800 kJ/kgK), thanks to which ash particles store heat, and its low thermal conductivity [143, 144, 146]. One of the benefits of fly ash is their specific weight, which is two to three times lower than other brake pad components. This means that the use of ash makes it possible to reduce the weight of the pad [143, 144, 149].
Figure 18
Figure 19
Figure 20
Cellulose is an organic material obtained from trees. It is most commonly added to brake pads in powdered form. The manufacture of brake pads usually involves high temperatures, burning the cellulose. This results in a porous material, which reduces the density of the final product. Also, the noise of braking is reduced [51]. Marewad et al. stated that the friction material containing 10wt% micro-cellulose fibres showed comparable results with the commercial brake pads. The wear rate of the prepared by them material was found to be 3.7mg/m. COF value was determined to be 0.357. They also say that thermal stability of prepared composite samples was very good up to 500&#;C [150]. However, this is rather due to the other components. So far in the automotive industry, cellulose friction materials are used in the production of specific types of clutches [151].
Copper is one of the basic components of brake pads. The effects of copper on the tribological properties of brake pads is strongly related to the copper content [152, 153, 154]. Research showed that fractions lower than 4% of volume do not yield significant results. Brake pads with more than 4% copper demonstrate an increased coefficient of friction. Drawbacks of using copper include a changing coefficient of friction as the pressure and speed of friction changes, demonstrated by many researchers [155, 156, 157]. A changing coefficient of friction may produce undesired noise [42]. Copper, like cast iron, creates contact zones during friction. This is because, despite being a soft material, copper is still usually harder and more resistant to abrasion than the binder. During abrasion it creates a film on the corresponding surface, increasing thermal conductivity and heat resistance of the brake pad [158]. Adding copper to brake pads may also support the process of recycling devices with electrical motors. The motor wiring can be simply cut into 1-2 mm pieces and provide a ready material for brake pad production [107]. Powdered copper is also used, with nano- (50-200 nm) or micro- (400-600 μm) particles [159]. Unfortunately, copper is harmful to humans and some states introduce regulations limiting the allowable fraction in brake pads. There is a need for a substitute material, which is successfully met by graphite and titanium mixtures. Additionally, the resulting material demonstrates reduced braking noise [42].
Figure 21
Boron is metalloid which is very commonly used in the industry. It is characterised by a high melting point. Also, it demonstrates low chemical activity. Boron is a good thermal and electrical isolator. Due to its advantageous properties it was studies as a friction material. Boron fraction in brake pads usually does not exceed 2% of volume. It is hard and therefore improves the durability of the pad, which corresponds to increased wear resistance [160]. Numerous researchers who studied brake pads containing boron observed that the element increases the coefficient of friction. However, it was also observed that when temperatures exceed 100&#;C, the coefficient significantly drops. This phenomenon may be explained by reduced hardness and melting of another component &#; aluminium [161, 162, 163]. On the other hand, it was observed that the coefficient of friction changes in a predictable manner, and the value decreases in a more stable and repeatable way compared to commercial pads [163, 164]. However, because of low thermal conductivity, boron makes it difficult to remove heat from friction points. This may lead to overheating and damage of the pad structure. Other studies have shown that friction materials containing boron have a coefficient of friction higher than ordinary, commercial brake pad &#; 0,495. Additionally, it has been found that such materials have thermal stability up to 200&#;C [165, 166].
Figure 22
Graphite is a material commonly used in the production of various lubricants [167, 168]. Both natural graphite and similar materials are used, e.g. s artificial graphite, and expanded graphite [169]. Depending on the structure, contamination, and operating conditions, it may have various (but mostly positive) effects on tribological properties [169, 170, 171]. Numerous studies demonstrate initial oxidation temperatures from relatively low (approximately 180-300&#;C [172, 173]) to high, up to 700&#;C [174]. Resistance to high temperatures makes graphite a favourable choice in the production of brake components for airplanes. There, brakes operate almost only in high temperatures, and therefore other properties are less important [168]. In automobile brake pads, graphite may be used as a substitute for copper because, as previously mentioned, it serves as an excellent lubricant. Graphite&#;s lubricating properties stem from its capacity for bonding with iron oxide particles released during brake disc oxidation, which then creates a thin film on the surface of the friction pair [175, 176]. That is why it contributes to the reduction of changes in the coefficient of friction with rising temperatures [51, 177, 178, 179], although researchers are not unanimous in this claim [168, 180]. As for the wear rate, its value is influenced by both wt% of graphite in friction material and the operating conditions: friction speed or contact pressure [181]. Graphite is a decent heat conductor, which improves heat removal from friction points. This protects the binder, which is usually more sensitive to high temperatures [42]. At the same time, graphite is an inexpensive material. It was also observed that the use of graphite has a positive effect on braking noise reduction [171]. Leonardi et al. stated that the size of the graphite particles also influences the tribological properties. The highest value of the friction coefficient (0.62±0.02) was recorded for the grains of 100 μm, while the lowest value of wear rate (4.2±0.2 m2/ N) for the smallest ones (below 40 μm) [182].Moreover, the particle size also influences TL (thermal localisation phenomenon). The best results were obtained for samples with a graphite size below 21mm [183].
Titanium is increasingly more common in the automotive industry. Its properties, which relate to the mineral&#;s crystal structure [184], among other things, made it a suitable candidate for a brake pad material. Titanium serves well as a copper substitute, especially in high temperatures, where its lubricating properties emerge. It also balances the changes of the coefficient of friction in line with rising temperatures. This results in reduced noise during braking. Titanium&#;s mechanical properties also contribute, by preventing the formation of film on the brake disc, due to low adhesion to iron [42]. Brake pads containing titanium are also less susceptible to brake fade [43, 185]. Unfortunately, the material is expensive, and therefore the price of titanium brake pads is also significantly higher. The density of titanium is one of its benefits. It is a light material and therefore has a positive effect on reducing the overall weight of the braking system. Some manufacturers add titanium to their brake pads in the form of potassium titanate. The compound yields excellent results in conjunction with phenol resin and aramid pulp. This connection creates a stable film on the brake disc, which ensures improved stability of the coefficient of friction and increased wear resistance, as the ceramic material particles (potassium titanate) adhere strongly to aramid fibres. The phenomenon also has a beneficial effect on the thermal resistance of the pad [186, 187, 188].
Figure 23
Figure 24
Brass is a metal used as a friction material. Different brass fractions result in varied tribological properties of brake pads. One of the most important changes is the reduction of the coefficient of friction and a positive impact on the coefficient&#;s changes in changing operating conditions. COF is less susceptible to changes with rising temperatures and friction speed. The pad&#;s wear rate also changes [189]. Some research showed that with higher brass fractions, the wear rate decreases, resulting in a longer operating life of the pad [190, 191]. Others claim that brass shortens the lifetime of the friction material, mainly when dealing with high-temperature friction [192]. That is because similarly to copper, brass improves thermal conductivity [191, 193]. Thus, more intense penetration of heat into the material takes place, which in turn accelerates the degradation of the matrix [192, 194]. Moreover, brass demonstrates lubricating properties. That is why increasing its fraction reduces the coefficient of friction [190], which may lead to longer stopping distance. Compared to other friction materials, brass is heavy. Increased content of brass therefore results in higher density of the final product.
Cast iron is usually used in the form of crushed chips up to 1 mmin size. The material has a positive effect on the tribological properties of brake pads [31, 195]. A 2-4% fraction of cast iron increases the coefficient of friction by adhesion on the meeting point of the friction surfaces. Cast iron is characterised by high resistance to abrasion, as it deforms under pressure to create contact areas with the brake disc in the form of ridges (other components wear more quickly by creating craters) [41, 196]. This increases the brake pad&#;s overall wear resistance. Different papers indicate that as friction speed and pressure increases, the coefficient of friction of brake pads with cast iron fraction may rise or fall. This is also affected by other additives, especially those with lubricating properties [158].
Figure 25
Figure 26
Steel is an alloy of iron and carbon, with a carbon fraction under 2.11%. It is a friction material which increases the coefficient of friction. Additionally, through its resistance to high temperatures, it stabilizes the coefficient [51]. Steel is also a decent heat conductor, which is important in terms of the durability of the pad. Excess heat may damage the binder, but in this case it is removed to other elements of the braking system [197]. Steel is most commonly added to brake pads in the form of steel wool [198], or in the form of fibres of various shapes and sizes [199, 200]. Alternatively, steel powder (such as RSB 100) may be used, whose geometrical properties (significant external surface) make it possible to reduce the percentage content of steel in the final product. A similar solution might also be used to reduce copper fractions [201]. This stems from the fact that powder metallurgy technology requires the use of solid lubricants, which later serve as lubrication of the brake pad-brake disc meeting point. Appropriate manufacture technology, taking into account forging and annealing the pad, instead of the regular pressure sintering, improves the mechanical properties of the final product (also ensuring increased hardness) [202, 203]. Unfortunately, high steel fraction in the pad leads to the formation of deep scratches in the disc, which is not desired. This is the result of decent adhesive properties, creating short-lasting connections which &#;tear&#; material from the friction pair [201]. This phenomenon, however, has its benefits. It makes the connection between the fraction material and the backing plate easier, greatly facilitating the production process [202]. The properties of steel described above make brake pads with high steel content serve well in brake systems in airplanes and in any other application requiring high and stable coefficient of fraction for the price of a significant wear ratio [204].
Figure 27
Figure 28
Zeolites are naturally occurring aluminosilicate minerals. Because their properties are similar to ceramics, Keskin [205] decided to use it as a component of brake pads. It was added in the form of a fine dust obtained by grinding, in proportions ranging from 5 to 35% of the pad&#;s weight. High temperature sintering made it possible to remove the natural water content in zeolites. Research showed that zeolite may be successfully used as a friction material in brake pads. Best results were observed in 10% mineral fractions. Zeolite causes the coefficient of friction to stabilize at 0.4-0.45, and have low sensitivity to temperature changes. Similar results were obtained by Chau et al. They performed tests in the temperature range of 150&#;300&#;C. An improvement in the anti-corrosion properties of the friction material containing zeolites has also been noted [206]. Its wear resistance also increases, extending the brake pad&#;s operating life [205].
No matter the industry, brake lining is essential to assure workers and products are kept safe. The Occupational Safety and Health Administration aims to identify workplace hazards and ensure safety is upheld.
It&#;s not difficult to see why maintaining your industrial brakes is essential. You want your brakes to do what they need to do: apply friction and slow down.
But what are the best materials for brake lining?
Keep reading for everything you need to know to choose the best friction material for your brakes.
Brake lining is a layer of asbestos or a similarly-functioning material attached to a brake shoe which creates friction against the brake drum.
This friction eventually slows a machine down, allowing it to stop.
Generally, there are three different categories of friction materials used in brake lining. We&#;ll explain the three types and the different subcategories below.
Organic brake linings are constructed from organic fibers, pressurized, and held together by glue. For example, coconut shells or other plant-derived fibers may be used to build organic brake linings.
Within the category of organic brake linings are asbestos and non-asbestos materials. Passenger cars no longer use asbestos brake linings because of their correlation to cancer. However, some industries may still use this lining today.
Asbestos brake linings were popular because they&#;re heat resistant while providing insulation.
Non-asbestos linings are more popular today, containing brass fillings to help dissipate heat. Within the non-asbestos category are three other linings:
These linings are made from sintered alloy, typically copper, brass, or steel. Sintered linings are created by fusing metallic particles using heat and pressure. This generates a product very resistant to friction.
These linings are C/C composites, made from carbon fiber. These linings are very thermally stable and lightweight, making them a popular choice for aircraft and race-cars.
The right brake pad linings for your machine will depend on machine type, type of braking system, budget, wear and tear, and environmental conditions.
Clean, quiet, and expensive brake linings may not work best in harsh environmental conditions.
Powerful friction material may mean more brake dust is being generated, requiring more frequent cleanings to ensure longevity.
Choosing the best friction material for industrial brake linings will depend on your budget, daily machine habits, and environmental conditions.
Be sure to take these factors into account when choosing the best brake lining for your machine.
For more articles on brakes and even industrial engineering materials, visit our blog today.
Are you interested in learning more about Inorganic wear-resistant powders? Contact us today to secure an expert consultation!